Paper | Title | Page |
---|---|---|
TUPOTK005 | Mitigation of Parasitic Losses in the Quadrupole Resonator Enabling Direct Measurements of Low Residual Resistances of SRF Samples | 1196 |
|
||
The quadrupole resonator (QPR) is a dedicated sample-test cavity for the RF characterization of superconducting samples in a wide temperature, RF field and frequency range. Its main purpose are high resolution measurements of the surface resistance with direct access to the residual resistance thanks to the low frequency of the first operating quadrupole mode. Besides the well-known high resolution of the QPR, a bias of measurement data towards higher values has been observed, especially at higher harmonic quadrupole modes. Numerical studies show that this can be explained by parasitic RF losses on the adapter flange used to mount samples into the QPR. Coating several micrometer of niobium on those surfaces of the stainless steel flange that are exposed to the RF fields significantly reduced this bias, enabling a direct measurement of a residual resistance smaller than 5 nano-Ohm at 2 K and 413 MHz. | ||
DOI • | reference for this paper ※ https://doi.org/10.18429/JACoW-IPAC2022-TUPOTK005 | |
About • | Received ※ 08 June 2022 — Revised ※ 12 June 2022 — Accepted ※ 16 June 2022 — Issue date ※ 28 June 2022 | |
Cite • | reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml) | |
TUPOTK016 | HiPIMS-Coated Novel S(I)S Multilayers for SRF Cavities | 1234 |
|
||
Funding: Material syntheses and characterizations via SMART, BMBF, Germany (05K19PSA). Superconducting characterizations via iFAST, H2020, EU (101004730). Part of this work via the MNaF, University of Siegen. Pushing beyond the existing bulk niobium SRF cavities is indispensable along the path towards obtaining more sustainable next generation compact particle accelerators. One of the promising candidates to push the limits of the bulk niobium is thin film-based multilayer structures in the form of superconductor-insulator-superconductor (SIS). In this work, S(I)S multilayer structures were coated by high power impulse magnetron sputtering (HiPIMS), having industrial upscaling potential along with provid-ing higher quality films with respect to conventional magnetron sputtering techniques (e.g., DCMS), combined with (PE)-ALD techniques for deposition of the ex-situ insulating layers. On the path towards formulating opti-mized recipes for these materials to be coated on the inner walls of (S)RF cavities, the research focuses on innovat-ing the best performing S(I)S multilayer structures con-sisting of alternating superconducting thin films (e.g., NbN) with insulating layers of metal nitrides (e.g., AlN) and/or metal oxides (e.g., AlxOy) on niobium lay-ers/substrates (i.e., Nb/AlN/NbN) in comparison to the so-called SS multilayer structures (i.e., Nb/NbN). This con-tribution presents the initial materials and superconduct-ing and RF characterization results of the aforementioned multilayer systems on flat samples. |
||
DOI • | reference for this paper ※ https://doi.org/10.18429/JACoW-IPAC2022-TUPOTK016 | |
About • | Received ※ 11 June 2022 — Revised ※ 14 June 2022 — Accepted ※ 15 June 2022 — Issue date ※ 18 June 2022 | |
Cite • | reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml) | |